420J2 stainless steel bar (06Cr13) is a martensitic stainless steel that can be hardened to HRC 50–55. For flat-form applications in the same grade, Walmay also supplies 420 stainless steel sheet and plate in cold-rolled and hot-rolled finishes from 0.5mm to 16mm.
| Element | C | Si | Mn | P | S | Cr |
|---|---|---|---|---|---|---|
| Content % | 0.26–0.35 | ≤1.0 | ≤1.0 | ≤0.040 | ≤0.030 | 12.0–14.0 |
Physical: Density 7.75 g/cm³, Melting Point 1480–1530℃, Strong magnetic
Mechanical (quenched & tempered): Tensile strength ≥1200MPa, Elongation ≥10%, Hardness HRC 50–55
Diameter: 6–100mm (Cold-drawn ±0.08mm, Hot-rolled ±0.15mm)
Length: 3–6m
Surface: Black (hot-rolled), Bright (cold-drawn, Ra≤1.6μm), optional grinding (Ra≤0.8μm)
Stainless Steel Bar Inventory Racking System
Spectrometer for Alloy Composition Analysis
Finished Stainless Steel Bars on Storage Racks
Palletized Stainless Steel Bars on Workshop Floor
Secured Stainless Steel Bar Bundles for Shipment
Forklift Loading Bundled Stainless Steel Bars into Freight Truck
Kitchen knives, surgical blades, stamping dies, milling cutter heads used in hardware processing facilities.
Bearings, valve seals, textile machine guides used in machinery manufacturing workshops.
Peelers, fruit knives, scissors blades used in kitchen workspaces.
Walmay will help match the right stainless product form and specification for your application, confirm quantities and packing needs, and provide requested documents based on order requirements.
Loading form…