Manufactured under ASTM and GB/T dual standards, it is stocked in thicknesses from 0.5mm to 16mm.
| Element | C | Si≤ | Mn≤ | P≤ | S≤ | Cr |
|---|---|---|---|---|---|---|
| Content (%) | 0.26–0.35 | 1 | 1 | 0.04 | 0.03 | 12.0–14.0 |
| Property | Annealed | Quenched & Tempered | Standard |
|---|---|---|---|
| Density | 7.75 g/cm³ | 7.75 g/cm³ | GB/T 7999 |
| Melting Point | 1480–1530℃ | 1480–1530℃ | - |
| Tensile Strength | ≥630 MPa | ≥1200 MPa | GB/T 228.1-2021 |
| Yield Strength | ≥440 MPa | ≥950 MPa | GB/T 228.1-2021 |
| Elongation | ≥20% | ≥10% | GB/T 228.1-2021 |
| Hardness (HB / HRC) | ≤223 HB | HRC 50–55 | GB/T 231.1-2009 |
| Salt Spray Resistance (Neutral) | ≥200h | ≥250h | ASTM B117 |
| Process Type | Thickness (mm) | Width (mm) | Length (mm) | Surface Finish | Tolerance |
|---|---|---|---|---|---|
| Cold Rolled | 0.5–6.0 | 1000/1219/1250 (Mill Edge) | 2000/2440/3000 | 2B / Polished (Ra≤1.6μm) | ±0.02mm |
| Hot Rolled | 6.0–16.0 | 1500/1800/2000 | 6000 (fixed) | NO.1 (Pickled) | ±0.1mm |
Customization Services:
Supports slitting (min width 50mm), laser cutting (any shape), and precision heat treatment. Hardness can be customized between HRC 45–55, eliminating additional post-processing. Custom widths up to 1500mm can be delivered within 7 days.
Stainless Steel Plate Bending/Stamping Process
Stainless Steel Plates on Storage Rack
Palletized Stainless Steel Plates
Stainless Steel Plate Rolling Line
Precision Thickness Inspection of Stainless Steel Plate
Forklift Loading Stainless Steel Plates for Shipment
Specification: 2.0mm × 1219 × 2440mm
Case: Used for kitchen knife blades. After quenching, hardness reached HRC 52, maintaining sharpness twice as long as carbon steel and reducing material loss by 15%.
Specification: 5.0mm × 1500 × 6000mm
Case: Applied in textile machinery guides. Walmay customized quenching achieved 3-year wear life, lowering maintenance cost by 60%.
Specification: 3.0mm × 1219 × 2440mm
Case: Used for stamping mold inserts. Polished surface (Ra≤0.8μm) ensured smooth release and extended mold service life to 18 months.
Specification: 4.0mm × 1219 × 2440mm
Case: Employed in industrial valve sealing rings. Hot-rolled 420 plate provided excellent hardness and moderate corrosion resistance, extending replacement intervals from 3 months to 1 year.
Walmay will help match the right stainless product form and specification for your application, confirm quantities and packing needs, and provide requested documents based on order requirements.