As Walmay’s cost-effective structural-grade material, 410 features high hardness and strong magnetism, making it ideal for mechanical components, construction fittings, and lightly corrosive environments. It is manufactured under ASTM and GB/T standards with full traceability.
| Element | C≤ | Si≤ | Mn≤ | P≤ | S≤ | Cr | Ni≤ |
|---|---|---|---|---|---|---|---|
| Content (%) | 0.15 | 1 | 1 | 0.04 | 0.03 | 12.0–14.0 | 0.6 |
| Property | Annealed | Quenched & Tempered | Standard |
|---|---|---|---|
| Density | 7.75 g/cm³ | 7.75 g/cm³ | GB/T 7999 |
| Melting Point | 1480–1530℃ | 1480–1530℃ | - |
| Tensile Strength | ≥520 MPa | ≥700 MPa | GB/T 228.1-2021 |
| Yield Strength | ≥345 MPa | ≥550 MPa | GB/T 228.1-2021 |
| Elongation | ≥20% | ≥15% | GB/T 228.1-2021 |
| Hardness (HB) | ≤200 | 300–350 | GB/T 231.1-2009 |
| Magnetism | Strong | Strong | - |
| Process Type | Thickness (mm) | Width (mm) | Length (mm) | Surface Finish | Tolerance |
|---|---|---|---|---|---|
| Cold Rolled | 0.3–6.0 | 1000/1219/1250 (Mill Edge) | 2000/2440/3000 | 2B / NO.4 (Brushed) | ±0.02mm |
| Hot Rolled | 6.0–16.0 | 1500/1800/2000 | 6000 (fixed) | NO.1 (Pickled) | ±0.1mm |
Customization Services:
Slitting (min width 50mm), laser cutting (any shape), and PE film coating available. Quenching and tempering options can be provided to meet specific hardness requirements, with 7-day delivery.
Stainless Steel Plate Bending/Stamping Process
Stainless Steel Plates on Storage Rack
Palletized Stainless Steel Plates
Stainless Steel Plate Rolling Line
Precision Thickness Inspection of Stainless Steel Plate
Forklift Loading Stainless Steel Plates for Shipment
Specification: 3mm × 1219 × 2440mm
Case: Used for agricultural machinery gear covers. After quenching, hardness reached HRC 42, tripling wear resistance over carbon steel and reducing cost by 35%.
Specification: 1.5mm × 1000 × 2000mm
Case: Applied to residential railing posts with NO.4 brushed finish. Strong magnetism allows easy installation and excellent outdoor corrosion resistance.
Specification: 2mm × 1219 × 2440mm
Case: Used as knife back material. Hot-rolled 410 plate provided high strength after heat treatment, ensuring stable mass production with <0.5% defect rate.
Specification: 5mm × 1500 × 6000mm
Case: Industrial fan housings made from NO.1 hot-rolled plates with passivation treatment, improving corrosion resistance by 20%.
Walmay will help match the right stainless product form and specification for your application, confirm quantities and packing needs, and provide requested documents based on order requirements.